Main Article Content

Abstract

Mortar is a mixture of adhesives (portland and lime cement), sand and water with certain compositions. Use of adhesive materials on building construction in general still use portland cement, but in terms of portland cement costs are required a greater cost. This study aims to determine the behavior of the compressive strength of mortar using Coconut Shell Charcoal (CCS) as a substitute for cement. The method of manufacture and testing of mortar compressive strength refers to SNI 03-6825-2002 with mortar 1Pc: 3Ps mortar. Range of initial flow values used is 105% - 115%. CCS used is pass No. 200 which utilizes combustion results from coconut shells. Variations of mortar test specimens were 0%, 2.5%, 5%, 7.5%, 10% and 12.5% respectively each variation had 10 sample specimens. Test sample was immersed for 27 days and compressive strength mortar test was performed at 28 days. Value compressive strength of mortar on variations of 0%, 2.5%, 5%, 7.5%, 10%, 12.5% are 25.11 MPa, 25.65 MPa, 26.07 MPa,27.00 MPa, 26.40 MPa and 25.98 MPa. The highest increase of mortar compressive value was variation of 7.5% by 7.51%.

Article Details

How to Cite
Sihombing, A. P., Afrizal, Y., & Gunawan, A. (2019). PENGARUH PENAMBAHAN ARANG BATOK KELAPA TERHADAP KUAT TEKAN MORTAR. Inersia: Jurnal Teknik Sipil, 10(1), 31–38. https://doi.org/10.33369/ijts.10.1.31-38

References

  1. ASTM C 270: Standard Specification for Mortar for Unit Masonry. American Standard Testing and Material.
  2. Moerdwiyono, 1998, Diktat Teknologi Bahan. Semarang.
  3. SNI 03-6225-2002: Metode Pengujian Kuat Tekan Mortar Semen Portland untuk Pekerjaan Sipil. Depertemen Pekerjaan Umum.
  4. SNI 03-6820-2002: Spesifikasi Agregat Halus untuk Pekerjaan Adukan dan Plesteran dengan Bahan Dasar Semen. Depertemen Pekerjaan Umum.
  5. SNI 03-6825-2002: Metode Pengujian Kekuatan Tekan Mortar Semen. Depertemen Pekerjaan Umum.
  6. SNI 03-6882-2002: Spesifikasi Campuran Mortar. Depertemen Pekerjaaan Umum.
  7. SNI S-04-1989-F: Persyaratan Air dalam Campuran beton dan Mortar.
  8. Depertemen Pekerjaan Umum.
  9. Sutikno, 2003, Pengaruh Penggunaan Abu Hasil Pembakaran Kayu pada Kuat Tekan Mortar, UNESA.
  10. Wardi, 2003, Pengaruh Pemakaian Arang Batok Kelapa terhadap Kuat Tekan Beton. Jurnal R & B, 3(1) PP. 27-34 ISSN 1412-5080 http://www.polinpdg.ac.id.
  11. Zahrina, I., 2007, Pemanfaatan Abu Sabut dan Cangkang Sawit sebagai Sumber Silika pada Sintesis ZSM-5. 31. Jurnal sains dan teknologi, 2007-academia.edu.