MORTAR SEMEN ABU DAUN PINUS DAN ABU BATA MERAH

Elhusna Elhusna(1), Yuzuar Afrizal(2), Halimatus Sofia(3),
(1) Universitas Bengkulu, Indonesia
(2) Universitas Bengkulu, Indonesia
(3) Universitas Bengkulu, Indonesia

Abstract


his article is a report research of mortar with 10% Pine leaf ash (PLA) and 5 variations of red brick ash (RBA). The mortar is a mixture of fine sand, water, and adhesive material with proportion of cement and fine sand is 1 dan 3. RBA was added up to 50% of cement with 10% addition for each variation. Both of the ashes were added base on the weight volume of cement of normal mortar. The normal mortar is the mortar without the ashes. The initial flow of the
mortar is 105%-115%. The 5 cm mortar cubes were made to test the compressive strength and the absorbtion. The tests were done according to SNI 03-6825-2002 and SNI 15-2049-2004 when the speciments age is 28 days. The cube speciments were taken out of the water sink a day earlier. The highest compressive strength is 22,4% higher than the normal mortar come out of
the PLA mortar without RBA. The strength of the PLA and 10% RBA mortar is 4,4% higher than the normal one and 18% lower then the PLA mortar without the RBA. The lowest mortar absorbtion (11,68%) belongs to PLA mortar with 10% RBA. The research result shows that the absorbtion and the compressive strength of the mortar isnot always inversely propotional.


Full Text:

PDF

References


Fauzi, M, F., dan Nursyamsi., 2014, Pemanfaatan Limbah Serbuk Kayu (Sawdust) sebagai Subtitusi Agregat Halus pada Campuran Beton, Teknik Sipil, Universitas Sumatera Utara.

Irawan, R, R., 2017, Kajian Sifat Kimia, Fisika, dan Mekanik Semen Portland di Indonesia, Pusat Litbang Jalan dan Jembatan Bandung.

Nurmawati, I., 2006, Pemanfaatan Limbah Industri Penggergajian Kayu sebagai Bahan Subtitusi Pembuatan Paving Block, Skripsi, Jurusan Pendidikan Teknik Bangunan, Program Studi TeknikSipil, Universitas Negeri Semarang.

Nurlina, S., Hidayat, T., Suseno, H., Kharisma, E, M., 2014, Pengaruh

Penggunaan Limbah Batu Bata sebagai Semen Merah terhadap Kuat Tekan dan Kuat Tarik Mortar, Skripsi, Jurnal Rekayasa Sipil, Vol.8, No.2, Jurusan Teknik Sipil, Fakultas Teknik, Universitas Brawijaya.

Ratnaningsih, A., Badriani, R, E., dan Arifin, S., 2014, Pengaruh Penambahan Sekam Padi pada Campuran Beton Ringan Non Struktural terhadap Nilai Penyerapan dan Nilai Kuat Tekan Beton Campuran Semen, Kulit Kopi, dan Flay Ash, Simposium Nasional RAPI XIII, Program Studi Teknik Sipil, Fakultas Teknik, Universitas Jember.

SNI 03-1968-1990, Metode Pengujian Analisis Saringan Agregat Halus dan Kasar, Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.

SNI 03-1970-1990, Metode Pengujian Berat Jenis dan Penyerapan Air Agregat Halus, Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.

SNI 03-1971-1990, Metode Pengujian Kadar Air Agregat, Departemen

Pekerjaan Umum Yayasan Badan Penerbit PU.

SNI 03-2816-1992, Metode Pengujian Kotoran Organik dalam Pasir untuk

Campuran Mortar dan Beton, Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.

SNI 03-4142-1996, Metode Pengujian Jumlah Bahan dalam Agregat yang

Lolos Saringan No.200 (0,075 mm), Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.

SNI 03-4804-1998, Metode Pengujian Bobot Isi dan Rongga Udara dalam

Agregat, Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.

SNI 03-6825-2002, Metode Pengujian Kekuatan Tekan Mortar Semen

Portland untuk Pekerjaan Sipil, Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.

SNI 03-6882-2002, Spesifikasi Mortar untuk Pekerjaan Pasangan, Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.

SNI 15-2049-2004, Semen Portland, Badan Standardisasi Nasional.

SNI 15-7064-2004, Semen Portland Komposit, Badan Standardisasi

Nasional.

Wikana, I., dan Gulo., 2012, Pengaruh Penambahan Tumbukan Bata Merah dan Pengurangan Semen terhadap Kuat Tekan Serta Keausan Paving Block, Jurusan Teknik Sipil, Universitas Kristen Immanuel

Yogyakarta.

Wiyano, B., dan Lukman, A, H., 1989, Analisis Kimia Daun Pinus dan

Pemanfaatannya, Jurnal Penelitian Hasil Hutan, Vol.6, No.2.




DOI: https://doi.org/10.33369/ijts.11.1.41-48

Article Metrics

 Abstract Views : 0 times
 PDF Downloaded : 0 times

Refbacks

  • There are currently no refbacks.


INERSIA partners :

 

INERSIA
Jurnal Teknik Sipil

Program Studi Teknik Sipil, Fakultas Teknik Universitas Bengkulu
Jln. W.R. Supratman, Kandang Limun, Bengkulu
Tlp.+62736-344087, 21170, Ext. 337, Fax +62736-349134
Email: inersia@unib.ac.id


ISSN 2086-9045

View My Stats