Bagasse ash and stone ash are materials that have some elements that fimilar to  cement elements. Bagasse ash is a waste that has not been utilized by community. Stone ash is a waste of stone crusher whose utilization in building structures is still lacking. This research was aimed to know compressive strength of the mortar which use bagasse ash and stone ash as a partial substitute of cement. The method of casting and compressive strength test of the mortar referred to SNI 03-6825-2002. The total of mortar cubes was 128 specimens with dimensions of 50 mm x 50 mm x 50 mm. Variations of bagasse ash and stone ash used were 5%, 10%, 15%, 20% and 25% of the weight of cement. The range of initial flow values used are 105%-115% (SNI 03-6882-2002). Mortar cubes cured for 27 days and test of mortar was conducted at 28th days. The value of mortar compressive strength variation of bagasse ash decrease from normal mortar compressive strength with a decrease respectively of 0.62%, 2.14%, 7.33%, 7.50% dan 9.53%. Compressive strengths of mortar with stone ash is increases from normal mortar in variations 5%, 10% and 15% with the percentages of 4.66%, 3.41% and 2.38% respectively, while in the variation of 20% and 25%  is decreases. Compressive strength of mortar with mixture bagasse ash and stone ash reduce from normal mortar with a decrease of 0.08%, 1.04%, 5.67%, 8.06% dan 15.12% respectively.

Article Details

License

Authors who publish with this journal agree to the following terms:

  1. Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
  2. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.
  3. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).
  4. This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
How to Cite
Sati, R. A., Supriani, F., & Afrizal, Y. (2019). PENGARUH VARIASI PENGGUNAAN ABU AMPAS TEBU (AAT) DAN ABU BATU (AB) SEBAGAI BAHAN PENGGANTI SEBAGIAN SEMEN TERHADAP KUAT TEKAN MORTAR. Inersia: Jurnal Teknik Sipil, 11(1), 13–18. https://doi.org/10.33369/ijts.11.1.13-18
Download Citation
Endnote/Zotero/Mendeley (RIS)
BibTeX

References

  1. Marzuki, I., 2009, Analisis Penambahan Additive Batu Gamping Terhadap Kualitas Komposisi Kimia Semen Portland, Jurnal Chemica Vo/. 10 Nomor 1 Juni 2009, 64-70, 65.
  2. Mulyati, S., Dahlan, D., dan Adril, E., 2012, Pengaruh Persen Massa Hasil Pembakaran Serbuk Kayu dan Ampas Tebu pada Mortar Terhadap Sifat Mekanik dan Sifat Fisisnya, jurnal ilmu fisika(JIF), vol 4 no 1, maret 2012, 32.
  3. Pandaleke, R., 2014, Kajian Eksperimental Sifat Karakteristik Mortar yang Menggunakan Abu Ampas Tebu sebagai Substitusi Parsial Semen, TEKNO SIPIL / Volume 12 / No.60 /April 2014, 57.
  4. Rachman, F., 2015, Penggunaan Abu Sekam Padi dan Abu Batu pada Pembuatan Genteng Beton, Digital Repository Universitas Jember, 15-16.
  5. SNI 03-1968-1990, Metode Pengujian Analisis Saringan Agregat Halus dan Kasar, Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.
  6. SNI 03-1970-1990, Metode Pengujian Berat Jenis dan Penyerapan Air Agregat Halus, Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.
  7. SNI 03-1971-1990, Metode Pengujian Kadar Air Agregat, Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.
  8. SNI 03-2816-1992, Metode Pengujian Kotoran Organik dalam Pasir untuk Campuran Mortar dan Beton, Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.
  9. SNI 03-4142-1996, Metode Pengujian Jumlah Bahan dalam Agregar yang Lolos Saringan No. 200 (0,075 mm), departemen Pekerjaan Umum Yayasan Penerbit PU.
  10. SNI 03-4804-1998, Metode Pengujian Bobot Isi dan Rongga Udara dalam Agregat, Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.
  11. SNI 03-6825-2002, Metode Pengujian Kekuatan Tekan Mortar Semen, Jakarta: Badan Standarisasi Nasional.
  12. SNI 03-6882-2002, Spesifikasi Mortar Untuk Pekerjaan Pasangan, Departemen Pekerjaan Umum Yayasan Badan Penerbit PU.
  13. SNI 15-2049-2004, Semen Portland, Jakarta: Badan Standarisasi Nasional.
  14. Wikana, I., dan Wantutrianus, Z. 2014. Pengaruh Pemakaian Fly Ash dan Abu Batu Sebagai Pengganti Sebagian Semen Pada Kuat Tekan Beton Mutu Tinggi. Majalah Ilmiah UKRIM Edisi 1/th XIX/2014, 45.