It is about steel JIS SCM4 of 0.39% C, 0.28% Si, 0.77% Mn, 0.95% Cr and 0.17% Mo composition. The steel was heated to improve the mechanical properties. The heat treatment was applied on  a cylindrical specimens of 20 mm diameter at 850 C for 30 minutes. The heated samples were then quenched into media of oil, coconut oil, kerosene, water and the other was annealed. The quenched specimens were tempered at 300 °C for 30 minutes. Testing of mechanical properties was tensile and hardness tests. The lower viscosity of the quenchant gave the tensile stress and hardness higher. The highest one  was about 1779 MPa and 52 HRC of specimens quenched to water and  the highest strain was achieved as high as to 21.76% of the annealed one. The microstructure of the  quench-temper was martensitic phase, and ferritic-pearlitic of the annealed.

Keywords

Steel JIS SCM 4 quench-temper cooling media annealing

Article Details

License
Lisensi Creative Commons
Ciptaan disebarluaskan di bawah Lisensi Creative Commons Atribusi-BerbagiSerupa 4.0 Internasional.
Author Biographies

Hendri Hestiawan, Mechanical Engineering University of Bengkulu

Material composites

Zuliantoni Zuliantoni, Mechanical Engineering University of Bengkulu

Manufacturing

Dwi Febriyanto, Mechanical Engineering University of Bengkulu

Mechanical Engineering

References

  1. Arifin, T., A., 2011, “Studi Pengaruh Variasi Suhu Quench Temper Terhadap Sifat Mekanik Dan Struktur Mikro Baja JIS SCM 4” Fakultas Teknik, Universitas Bengkulu, Bengkulu.
  2. Daryanto, 2010, “proses pengolahan besi dan baja (ilmu metalurgi)”, cetakan ke satu. PT.Sarana Tutorial Nurani Sejahtera.Bandung
  3. Sharma Rajan, C.P & Sharma Ashok., 1997,“Heat Treatment Principles and Techniques”., Prentice Hall of India, New Delhi.
  4. Sularso., & Kiyokatsu.s.,2002, “Dasar Perencanaan dan Pemilihan Elemen Mesin”, cetakan kesepuluh. PT. Pradnya Paramita. Jakarta.
  5. Surdia, T., & Saito. S., 2000, “ Pengetahuan Bahan Teknik”, Cetakan Kelima. PT. Pradnya Paramita. Jakarta.
  6. VanVlack L.H., 1991, “Ilmu dan Teknologi Bahan (Ilmu Logam dan Bukan Logam)”, Cetakan kedua, PT. Erlangga. Jakarta
  7. Wahyudi, Tedi., 2010, “Studi Pengaruh Temperatur Tempering Terhadap Sifat Mekanik Dan Struktur Mikro Baja AISI 4140” Fakultas Teknik, Universitas Bengkulu, Bengkulu.
  8. Yuwono. A. H., 2009., “Karakterisasi Material Pengujian Merusak (Destructive Testing)” Departemen Metalurgi dan Material Fakultas Teknik Universitas Indonesia. Depok.