Isi Artikel Utama

Abstrak

In composite engineering, there are also known hybrid composite types which allow the presence of two or more reinforcing particles and are usually arranged by a straight type and a random type. In this research, hybrid composites are made from a combination of kevlar fiber and carbon twill fiber using the vacuum assisted resin infusion (VARI) method. This fiber will be made into a composite consisting of ten layers with a composition of six layers of kevlar fiber and 4 layers of carbon twill fibers. Vinylester resin is used as a matrix on the composite. The hybrid composite material was given post curing treatment and soaked by sea water. From the tensile test results obtained an average ultimate tensile strength (UTS) value of 314.38 MPa at post curing temperature of 100 °C, then the results of compressive test of the kevlar/carbon hybrid composite with ASTM D6641 obtained an average compress strength value of 87.76 MPa at 100 °C postcuring and the results of the kevlar + carbon-vinylester composite shear test with ASTM D5379 obtained an average shear strength value of 20.45 MPa at post curing room temperature.

Rincian Artikel

Lisensi
Lisensi Creative Commons
Ciptaan disebarluaskan di bawah Lisensi Creative Commons Atribusi-BerbagiSerupa 4.0 Internasional.
Cara Mengutip
Suryono, A. F., Faizal, A., & Hestiawan, H. (2020). PENGARUH POST CURING TREATMENT DAN PERENDAMAN AIR LAUT PADA KOMPOSIT HYBRID KEVLAR/KARBON. Rekayasa Mekanika: Jurnal Ilmiah Teknik Mesin, 4(1), 13–17. https://doi.org/10.33369/rekayasamekanika.v4i1.13273
Unduh Sitasi
Endnote/Zotero/Mendeley (RIS)
BibTeX

Referensi

  1. Jones, “Mechanics of Composite Materials”, Washington D.C., USA, 1975.
  2. Schwartz, “Composite Materials Hand Book”, New York, 1984 .
  3. Diharjo dan Triyono, “Buku Pegangan Kuliah Material Teknik”, Universitas Sebelas Maret, Surakarta, 2003.
  4. William D. Callister, Jr., “Fundamentals of Materials Science and Engineering”, Department of Metallurgical Engineering, University of Utah, 2001.
  5. Onny, “Proses pembuatan serat carbon”, 2016.
  6. Tamaela, V, “Karakteristik Curing 80oC dan 100oC Komposit Serat E-Glass”, Skripsi Teknik Mesin, Fakultas Sains dan Teknologi, Universitas Sanata Dharma. Yogyakarta, 2016.
  7. Febriyanto, S., “Penggunaan Metode Vacuum Assited Resin Infusion Pada Bahan Uji Komposit Sanwidch Untuk Aplikasi Kapal Bersayap Wise-8”, Skripsi, 2011.
  8. ASTM D3039, “Standard Test Method for Tensile Properties”.
  9. ASTM D6641, “Standard Test Method for Compressive Properties”.
  10. ASTM D5379, “Standard Test Method for Shear Properties”