This was the work in one of the Gas-Steam Power Plant (PLTGU) in the Southern Sumatra. The compressors on the Alsthom gas turbine suffered damage to the rotor blade section causing it to stop operations. In this study discussed the analysis of the cause of damage to the axial compressor rotor blade with the aim of knowing the causative factors of damage, the mechanism of damage, the shape of the microstructure and the size of the grain. Observations are made by direct macro observations. After making observations, it continues with the analysis of observations. From the results of the analysis, it was concluded that the damage occurred was influenced by several factors, namely corrosion, service life and environmental conditions. If the damage is compared to the size of the grain then the part that is a lot of damage has a larger grain size compared to the slightly damaged part.

Rincian Artikel

Lisensi
Lisensi Creative Commons
Ciptaan disebarluaskan di bawah Lisensi Creative Commons Atribusi-BerbagiSerupa 4.0 Internasional.
Biografi Penulis

Ahmad Rizki Maulana Nasution, Teknik Mesin

Mahasiswa

Hendri Hestiawan, Teknik Mesin

Dosen, Lektor Kepala

Ahmad Fauzan Suryono, Teknik Mesin

Dosen, Lektor
Cara Mengutip
Maulana Nasution, A. R., Hestiawan, H., & Suryono, A. F. (2022). Failure Analysis of Axial Compressor Rotor Blade on Alshtom Gas Turbine with Capacity 20 MW at PLTGU. Rekayasa Mekanika: Jurnal Ilmiah Teknik Mesin, 5(2), 35–40. https://doi.org/10.33369/rekayasamekanika.v5i2.20172
Unduh Sitasi
Endnote/Zotero/Mendeley (RIS)
BibTeX

Referensi

  1. Syuk, M,F., 2015, Evaluasi Kerusakan Akibat Korosi Pada Sudu Kompresor Aksial Turbin Gas Kapasitas 21,6 MW di PT. PLN (Persero) Teluk Lembu Pekanbaru, Laporan Kerja Praktik, Program Studi Teknik Mesin, Universitas Riau, Pekanbaru.
  2. Renardi, R., 2018, Analisis Kegagalan Ring Segment Cobalt Base Superalloys X40 Pada Turbin Gas Pembangkit Listrik PT. X, Skripsi, Institut Teknologi Sepuluh November, Surabaya.
  3. Linden, D., 2011, Long Term Operating Experience with Corrosion Control in Industrial Axial Flow Compressors, Proceedings of The Fortieth Turbomachinery Symposium, 12-15 September, Houston, Texas, 93–106.
  4. Adrian, J., 2016, Analisa Kerusakan Superheater Tube Boiler Tipe ASTM A213 Grade T11 Pada Pembangkit Listrik Tenaga Uap, Skripsi, Institut Teknologi Sepuluh November, Surabaya.
  5. Sutowo, C., Senopati, G., Kartika, I., dan Priyono, B., 2016, Analisa Kegagalan Retak Material Besi Cor Kelabu, Proceeding Universitas Pamulang, Vol. 1, No. 1, 50–57.
  6. Oktavianto, D. D., 2019, Analisis Pengaruh Variasi Media Pendingin Terhadap Kekerasan dan Struktur Mikro Besi Cor Kelabu FC 25 Dengan Mangan 1,2 %, Skripsi, Universitas Sanata Dharma, Yogyakarta.
  7. Surdia,T. dan Saito, S., 1999, Pengetahuan Bahan Teknik, 4th ed. Jakarta: PT. Pradnya Paramita.
  8. Hutauruk, F. Y., 2017, Analisa Laju Korosi Pada Pipa Baja Karbon dan Pipa Galvanis dengan Metode Elektrokimia, Skripsi, Institut Teknologi Sepuluh November, Surabaya.