SINTESIS METIL ESTER DARI LIMBAH KELAPA SAWIT DENGAN SONOCHEMISTRY DAN CRACKING MENJADI BIOFUEL DENGAN KATALIS CrMo/HZ

Jertadi Putri Dhani(1), Agus Sundaryono(2), Dewi Handayani(3),
(1) Universitas Bengkulu, Indonesia
(2) Universitas Bengkulu, 
(3) Universitas Bengkulu, Indonesia

Abstract


This study aims to calculate the percentage methyl ester converted to biofuel through catalytic cracking reaction,analyzes component and determine characteristics using catalyst CrMo/HZ. This research begins with impregnation sample preparation which includes heating oil,degumming,bleaching and determination free fatty acid (FFA). Methyl ester obtained from liquid waste conversion crude palm oil through an esterification and transesterification reaction with H2SO4 and NaOH catalyst with sonochemistry methode is a method that utilizes ultrasonic waves origanating from a device is ultrasonic cleaner for one hour at temperature 60oC. The methyl ester obtained was cracked with a CrMo/HZ catalyst which was carried out for 2 hours at temperatur 380oC. To find out the components of compounds formed in methyl ester, an analysis was performed using GCMS then characteristics of biofuel are determined from the result of catalytic cracking obtained through acid number testing,density,viscosity,pour point and fog point. The result obtained from the conversion of methyl ester to biofuel with Crmo/HZ Catalyst Is 60,17% And For Testing The Physical Characteristics Of Biofuel Namely The Acid Number 1,87 Mg KOH/G, density 0,804 g/cm3, viscosity 1,162 Cst, pour point 0oC and fog point 1,4oC. The result of cracking produce a consituent component of biofuel namely gasoline 33,67%, kerosene 16,26%, gas oil 10,24% beside that, there are still methyl ester as much as21,89%.


Full Text:

PDF

References


Sa’adaha, A.F., Akhmad Fauzib, Bambang Juanda, Peramalan Penyediaan dan Konsumsi Bahan Bakar Minyak Indonesia dengan Model Sistem Dinamik Jurnal Ekonomi dan Pembangunan Indonesia, 2017: 17( 2): 118–137

Noviyanti, A.R., Yati B. Yuliyati, Diana Rakhmawaty Eddy,Solihudin, Roekmiati Tjokronegoro, Struktur Dan Morfologi Elektrolit Apatit Lantanum Silikat Berbahan Dasar Silika Sekam Padi, Jurnal Material dan Energi Indonesia , 2016: 6(2): 1 – 6.

Afrina ,Y., Pengaruh Pertumbuhan Ekonomi Dan Penduduk Terhadap Konsumsi Energi Di Indonesia , Jom FEKON , 2015 : 2(2): 1-14.

Kartiasiha,F., Yusman Syaukat, Lukytawati Anggraeni, Determinan Intensitas Energi di Indonesia , Jurnal Ekonomi dan Pembangunan Indonesia, 2012: 12 (2): 192-214.

Wijayantia, W., Mega Nur Sasongko, Christia Meidiana, Lilis Yuliati, Metode Pirolisis Untuk Penanganan Sampah Perkotaan Sebagai Penghasil Bahan Bakar Alternatif, Jurnal Rekayasa Mesin , 2013: 4 (2): 85-92

Mohanty, B., Ismail Ismail Abdullahi Bioethanol Production from Lignocellulosic Waste-A Review, Biosciences Biotechnology Research Asia, 2016 : 13(2): 1153-1161

Wahyu P, M.A., Nely Ana Mufarida, Kosjoko, Pengaruh Prosentase Penambahan Ethanol Pada Bahan Bakar Pertalite Terhadap Daya Dan Torsi Pada Mesin Motor Matic 125 CC, J-Proteksion , 2019: 3 (2 ): 15-28

Widayana, G., Bio-Diesel Dari Tanaman Jarak Pagar Sebagai Bahan Bakar Pengganti Solar, JPTK, Undiksha, 2010: 7 (2): 47 - 58

Hamid S. T., Rachman Yusuf, Preparasi Karakteristik Biodiesel Dari Minyak Kelapa sawit, Makara, Teknologi,2002: 6 (2): 60-65.

Rahardjo, P.N., Studi Banding Teknologi Pengolahan Limbah Cair Pabrik Kelapa Sawit, J. Tek.Ling, 2009: 10 (1): 9 – 18.

Yulastri, Ariadi Hazmi, Reni Desmiarti, Aplikasi Plasma Dengan Metoda Dielectric Barrier Discharge (DBD) Untuk Pengolahan Limbah Cair Kelapa Sawit, Jurnal Nasional Teknik Elektro,2013: 2 (2): 46-50.

Muryati., T.S., Agus Sundaryono, Dewi Handayani, Pembuatan Biofuel dari Limbah Cair PMKS dengan Katalis MoCo-HZ, Alotrop: 2018 : 2(2): 161-165.

Lestari, S., Agus Sundaryono, Rina Elvia. Preparasi dan Karakterisasi Katalis Mo-Ni/HZ dengan Metode Impregnasi untuk Cracking Katalitik Minyak Limbah Cair Pengolahan Kelapa Sawit menjadi Bahan Bakar Nabati, Alotrop, 2019: 3(1): 91-97

Sari,D.K.,Agus Sundaryono,Dewi Handayani,Uji Biofuel Hasil Perengkahan Metil Ester Dari Limbah Cair Pabrik Minyak Kelapa Sawit Dengan Katalis MoNi/HZ, Alotrop,2017: 1(2): 127-131.

Ningtyas, D.P., Siti Ari Budhiyanti, Latif Sahubawa, Pengaruh Katalis Basa (NaOH) Pada Tahap Reaksi Transesterifikasi Terhadap Kualitas Biofuel Dari Minyak Tepung Ikan Sardin, Jurnal Teknosains, 2013: 2(2): 103-114.

Makalalag, A., Pembuatan Metil Ester Dari Minyak Kelapa, Jurnal Penelitian Teknologi Industri , 2018: 10 (2): 67-74.

Firdaus, M.A., Perkembangan Biodiesel Di IndonesiaTinjauan Atas Kondisi Saat Ini, Teknologi Produksi &Analisis Prospektif, Jurnal PASTI , 2015: 9(1): 35–45

Sudradjat ,R., Yogie, S. ,D. Hendra , D. Setiawan , Pembuatan Biodiesel Biji Kepuh Dengan Proses Transesterifikasi, Jurnal Penelitian Hasil Hutan , 2010: 28 (2): 145-155.

Yelmida, Ida Zahrina, Fajril Akbar, Perengkahan PFAD (Palm Fatty Acid Distillate) Dengan Katalis Zeolit Sintesis Untuk Menghasilkan Biofuel, Jurnal Rekayasa Kimia dan Lingkungan , 2012: 9 (1): 45-50.

Salamah, S., Maryudi, Proses Pirolisis Limbah Styrofoam Menggunakan Katalis Silika-Alumina, Jurnal Rekayasa Kimia dan Lingkungan , 2018: 13 (1); 1 – 7.

Nugrahaningtyas,K.D.,Eko Cahyono, Dian Maruto Widjonarko, Reaksi Perengkahan Parafin Dengan Katalis NiMo/Zeolit Alam Aktif (ZAA): Efek Temperatur Pada Aktivitas Katalitik, Alchemy, (2015) : 11 (2) : 111-126

Anwaristiawan,D.,Harjito, Nuni Widiarti, Modifikasi Katalis BaO/Zeolit Y pada Reaksi Transesterifikasi Minyak Biji Jarak (Jatropha Curcas L.) menjadi Biodiesel, Indo. J. Chem. Sci, 2018: 7 (3) : 292-298.

Sisca, V., Aplikasi Katalis Padat Dalam Produksi Biodiesel, Jurnal Zarah, 2018 : 6(1): 30-38

Aziz, I., Siti Nurbayti, Arif Rahman, Penggunaan Zeolit Alam sebagai Katalis dalam Pembuatan Biodiesel, Valensi , Vol. 2 No. 4, Mei 2012 (511-515)

Kusdarto, Potensi Zeolit Di Indonesia, Jurnal Zeolit Indonesia, 2008: 7 (2): 78 – 87.

Setyawan PH, D., Triyono, Morina, Aktivitas Katalis Ni/Zeolit pada Konversi Katalitik Metil Ester Minyak Goreng Jelantah (Mewco) pada Temperatur 450OC Menjadi Senyawa Fraksi Bahan Bakar, Lembaran Publikasi Lemigas,2009: 43(1): 65 – 74.

Fitriana , N., Rusmini, Pembuatan Zeolit Alam Teraktivasi HCl Dan Karakterisasinya , UNESA Journal of Chemistry , 2019: 8 (1): 17-19.

Erlina, N.O., Suci Amalia, Susi Nurul K, Preparasi, Modifikasi Dan Karakterisasi Katalis Bifungsional Sn-H-Zeolit Alam Malang, ALCHEMY,2013:2(3):154 –161

Efiyanti,L., Darma Santi, Pengaruh Katalis NiO Dan NiOMoO Terhadap Perengkahan Minyak Cangkang Biji Jambu Mete, Jurnal Penelitian Hasil Hutan, 2016: 34(3): 189-197.

Sugianto, D.J., Karna Wijaya, Iqmal Tahir, Karakterisasi dan Aplikasi Katalis Nikel-Molibdenum Teremban pada Zeolit Alam Aktif untuk Hidrorengkah Tir Batubara, Jurnal Natur Indonesia , 2014: 16(1): Jurnal Natur Indonesia: 10–22.

Susgadarsukawati, N.F., Sigit Priatmoko, Sri Wahyuni, Preparasi Dan Karakterisasi Katalis Ni-Mo/Zeolit Alam Sebagai Katalis Perengkahan Sampah Plastik HDPE , Indo. J. Chem. Sci, 2012: 1 (1) : 68-73.

Bustamam,H., Syaiful Bahri, Amun Amri, Pembuatan Bio-Oil Dari Kayu Cemara (Causarina Equisetifolia L.) Dengan Teknologi Pirolisis Menggunakan Katalis MO/NZA, Jom FTEKNIK , 2016, 3(2): 1-8.

Trisunaryanti, W., Optimasi Waktu dan Rasio Katalis/Umpan pada Proses Perengkahan Katalitik Fraksi Sampah Plastik Menjadi Fraksi Bensin Menggunakan Katalis Cr/Zeolit Alam, Indonesian Journal of Chemistry, 2002 : 2(1), 30-40

Rahayu,F.L., Rahmad Nuryanto, Linda Suyati, Pengaruh Diameter Kanal Pelet Katalis Zeolit Aktif dan Ni-Zeolit terhadap Pirolisis Limbah Batang Pohon Sagu (Metroxylon sp.), Jurnal Kimia Sains dan Aplikasi , 2013: 16(1) : 33–37

Budiyanto,R., Donatus Setyawan, Novita Andarini, Aktivitas Dan Selektivitas Katalis Ni/H5NZA Terhadap Hidrorengkah Metil Oleat Menjadi Senyawa Hidrokarbon Fraksi Pendek, Jurnal Kimia Riset, 2018 : 3(1): 58-70.

Rodiansono, Wega Trisunaryanti, Triyono, Pembuatan, Karakterisasi Dan Uji Aktivitas Katalis NiMo/Z Dan NiMo/Z-Nb2O5 Pada Reaksi Hidrorengkah Fraksi Sampah Plastik Menjadi Fraksi Bensin, Berkala MIPA,2007: 17 (2) : 43-53.

Dahyaningsih, E., Rahmasari Ibrahim, Achmad Roesyadi., Pembuatan Biofuel dari Minyak Nyamplung (Calophyllum inophyllum L) Melalui Proses Hydro cracking dengan Katalis Ni-Mo/ Zeolit, Jurnal Teknik POMITS , 2013: 2(1): 1-5.

Armalita,R.D., Syaiful Bahri, Yusnimar, Pembuatan Biodiesel Dari Minyak Biji Bintaro Dengan Reaksi Trans esterifikasi Dan Katalis Lempung, , JOM FTEKNIK, 2015: 2 (2): 1-6.

Santi, D., Lisna Efiyanti, Hidrorengkah Minyak Laka Menggunakan Katalis NiO/ Zeolit Alam Aktif Menjadi Fraksi Berpotensi Energi, Jurnal Penelitian Hasil Hutan, 2014: 32 (2): 93-102.

Badriyah, L., Iip Izul Falah, Produksi Gasoline Dari Minyak Kelapa Sawit Menggunakan Katalis Ni-MCM-41 Dan Co/Ni-MCM-41, Jurnal Kimia Dan Pendidikan Kimia, 2017: 2(1): 22-28.

Wijanarko,A.,Dadi Ahmad Mawardi, Mohammad Nasikin, Produksi Biogasoline Dari Minyak Sawit Melalui Reaksi Perengkahan Katalitik Dengan Katalis ?-Alumina, Makara, Teknologi, 2006: 10 (2): 51-60

Nugroho, A.N.P., Dwi Fitriyanto, Achmad Roesyadi, Pembuatan Biofuel dari Minyak Kelapa Sawit melalui Proses Hydrocracking dengan Katalis Ni-Mg/?-Al2O3, Jurnal Teknik POMITS,2014:3(2) : F117-F121.

Suminta, S., Karakterisasi Zeolit Alam dengan Metode Difraksi Sinar-X, Jurnal Zeolit Indonesia , 2006: 5(2): 52-68.

Ngapa, Y.D., Kajian Pengaruh Asam-Basa Pada Aktivasi Zeolit Dan Karakterisasinya Sebagai Adsorben Pewarna Biru Metilena, Jurnal Kimia Dan Pendidikan Kimia (JKPK), 2017: (2): 90-96

Aidha, N.N., Aktivasi Zeolit Secara Fisika Dan Kimia Untuk Menurunkan Kadar Kesadahan (Ca dan Mg) Dalam Air Tanah, J. Kimia Kemasan, 2013: 35 (1): 58-64

Atikah,W.S.,Potensi Zeolit Alam Gunung Kidul Teraktivasi Sebagai Media Adsorben Pewarna Tekstil, Arena Tekstil 2017: 32 (1): 17-24

Pardoyo, Listiana,Adi Darmawan, Pengaruh Perlakuan HCL Pada Kristalinitas Dan Kemampuan Adsorpsi Zeolit Alam Terhadap Ion Ca2+, Jurnal Sains & Matematika (JSM), 2009: 17(2) : 100-104.

Mahaddilla, F.M., Ardian Putra, Pemanfaatan Batu Apung Sebagai Sumber Silika Dalam Pembuatan Zeolit Sintetis, Jurnal Fisika Unand ,2013:2 (4): 262-268.

Windarti, T., Ahmad Suseno, Preparasi Katalis Zeolit Alam Asam Sebagai Katalis Dalam Proses Pirolisis Katalitik Polietilena , J. Kim.Sains & Apl,2004:7(3): 72-77.

Rianto, L.B., Suci Amalia, Susi Nurul Khalifah, Pengaruh Impregnasi Logam Titanium Pada Zeolit Alam Malang Terhadap Luas Permukaan Zeolit, Alchemy, 2012: 2(1): 58-67

Adriatia, M., Ahmad Susenoa, Taslimah, Modifikasi Zeolit Alam Menggunakan Besi (Fe) dan Kobalt (Co) untuk Katalis Degradasi Fenol, Jurnal Kimia Sains dan Aplikasi , 2013: 16(1) : 1 –5.

Erlina, N.O., Suci Amalia, Susi Nurul K, Preparasi, Modifikasi Dan Karakterisasi Katalis Bifungsional Sn-H-Zeolit Alam Malang , Alchemy, 2013: 2 (3): 154 – 161.

Hafiz, F., Zuchra Helwani,Edy Saputra, Sintesis Katalis Basa Padat Nanomagnetik CaO/Serbuk Besi untuk Reaksi Transesterifikasi Minyak Sawit Off Grade menjadi Biodiesel, Jom FTEKNIK , 2017: 4 (1): 1-10.

Aziz, I., Siti Nurbayti, Badrul Ulum, Esterifikasi Asam Lemak Bebas Dari Minyak Goreng Bekas, Valensi, 2011: 2(2): 384?388

Sumangat, D.,Tatang Hidayat, Karakteristik Metil Ester Minyak Jarak Pagar Hasil Proses Transesterifikasi Satu Dan Dua Tahap, J.Pascapanen , 2008: 5(2): 18-26.

Hastuti, Z.D., Dwi Husodo Prasetyo, Erlan Rosyadi, Pemanfaatan CPO Asam Lemak Bebas Tinggi Sebagai Bahan Bakar, Jurnal Energi dan Lingkungan , 2015: 11(1): 61-66

Prihanto , A., T. A. Bambang Irawan, Pengaruh Temperatur, Konsentrasi Katalis Dan Rasio Molar Metanol-Minyak Terhadap Yield Biodisel Dari Minyak Goreng Bekas Melalui Proses Netralisasi-Transesterifikasi, Metana , 2017 : 13(1) : 30-36

Fitriyana, L.A., Soeprodjo, Sri Kadarwati, Produksi Biodiesel Dari Dedak Padi (Rice Bran) Melalui Dua Tahap Reaksi In-Situ, Indonesian Journal of Chemical Science : 2012:1(2): 140-146.

Yuliani, F., Mira Primasari, Orchidea Rachmaniah , M. Rachimoellah, Pengaruh Katalis Asam (H2SO4) dan Suhu Reaksi pada Reaksi Esterifikasi Minyak Biji Karet (Hevea brasiliensis) menjadi Biodiesel, Jurnal Teknik Kimia, 2008: 3(1): 171-177.

Gusviputri, A., Njoo Meliana P. S., Aylianawati, Nani Indraswati, Pembuatan Sabun Dengan Lidah Buaya (Aloe VERA)

Sebagai Antiseptik Alami, Widya Teknik , 2013: 12 (1): 11-21

Astuti, Sulastriya Ningsi, Sintesis Dan Karakterisasi Nano Partikel Titanium Dioksida (TiO2) Menggunakan Metode Sonokimia, Jurnal Ilmu Fisika (JIF), 2017: 9 (1): 26- 32.

Kholidah, N., Pengaruh Temperatur Terhadap Persentase Yield Pada Proses Perengkahan Katalitik Sampah Plastik Menjadi Bahan Bakar Cair, Alkimia : Jurnal Ilmu Kimia dan Terapan, 2018 : 2(1): 28-33.

Prayoga , N., Bambang Sudarmanta, Studi Eksperimental Pengaruh Variasi Temperatur Bahan Bakar Terhadap Penyalaan Awal dan Unjuk Kerja serta Emisi Motor Honda Cb150r Berbahan Bakar Bioetanol E100, Jurnal Teknik ITS , 2015: 4(1): 1-7.

Mursiti, S., Ratna Dewi Kusumaningtyas, Sabirin Matsjeh, Jumina, Mustofa, Sintesis Fatty Acid Methyl Esther Dari Minyak Biji Mahoni (Swietenia Macrophylla, King) Dan Uji Performancenya Sebagai Bahan Bakar Alternatif Pada Mesin Diesel, Jurnal Sains dan Teknologi (Sainteknol), 2014 : 12(1): 41-48.


Article Metrics

 Abstract Views : 0 times
 PDF Downloaded : 0 times

Refbacks

  • There are currently no refbacks.


Alotrop indexed by :

           

ALOTROP

Program Studi Pendidikan Kimia Gedung Dekanat FKIP UNIB Lantai 2
Jl WR Supratman Kandang Limun Bengkulu
Telp/Fax (0736) 21170
e-mail : alotrop.fkip@unib.ac.id

View My Stats