The objective of this research was to utilize bintaro shell waste (Cerbera odollam). The morphology of bintaro shell is similar with coconut shell and the contains of lignin and cellulose is higher than coconut. Bintaro shell waste used as activated charcoal to remove environmental pollution caused by synthetic dyes waste of batik industry. The adsorbents were then applied to remove of Reactive Red-120 (RR) and Reactive Blue-198 (RB) dyes in aqueous solution using Visible Spectrophotometer analysis method. Bintaro shell was dried, cut and carbonized at 400°C for 1 hour, then activated with ZnCl2 20% for 24 hours at 27°C and dryed in oven at 105°C for 30 minutes. The activated charcoal of bintaro shell has proven afford to adsorbing RR and RB dyes. The optimum conditions (pH, contact time, adsorbent weight and temperature) were determined to obtain best adsorption capacity. The optimum of conditions for RR occured at pH 2, contact time of 40 minutes and adsorbent weight 100 mg while RB occurred at pH 11, contact time of 60 minutes and adsorbent weight 50 mg and with each the temperature 30°C. At optimum conditions the adsorption isotherm followed Freundlich model with maximum adsorption capacity obtained for RR and RB were 332.6 and 243.9 mg/g, respectively.

Article Details

License

Authors who publish with this journal agree with the following terms:

  1. Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
  2. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.
  3. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).
  4. This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
How to Cite
Aisyahlika, S. Z., Firdaus, M. L., & Elvia, R. (2019). KAPASITAS ADSORPSI ARANG AKTIF CANGKANG BINTARO (Cerbera odollam) TERHADAP ZAT WARNA SINTETIS REACTIVE RED-120 DAN REACTIVE BLUE-198. ALOTROP, 2(2). https://doi.org/10.33369/atp.v2i2.7483
Download Citation
Endnote/Zotero/Mendeley (RIS)
BibTeX

References

  1. Sri Utami, Lailan Syaufina, Noor Farikhah Haneda .,Daya Racun Ekstrak Kasar Daun Bintaro (Cerbera odollam Gaertn.) Terhadap Larva S Podoptera litura Fabricus , Jurnal Ilmu Pertanian Indonesia, 2010 : 15(2): 96-100 .
  2. Handoko, T., Suhandjaja, G., dan Muljana, H. Hidrolisis Serat Selulosa dalam Buah Bintaro Sebagai Sumber Bahan Baku Bioetanol. Teknik Kimia Indonesia. 2012 : 11 (1) : 26-33.
  3. Rienstra M., Bonten M.J.M., dan Gaillard C.A.J.M. Ceftriaxone-Associated Biliary Pseudolithiasis. The Journal Of Medicine. 2009: 67 (3) : 113-114.
  4. Soesanthy, F., Gusti, I., dan Balittri. Bintaro (Cerbera manghas) Sebagai Pestisida Nabati. Penelitian dan Pengembangan Tanaman Industri. 2011 : 17 (1) : 7-9.
  5. Bosalina, T. T., Etty R., dan Sri S. Pengaruh Aktivasi Fisika dan Kimia Arang Aktif Buah Bintaro Terhadap Daya Serap Logam Berat Krom. Biopropal Industri. 2016 : 7 (1) : 35-45.
  6. Suryani, I., M. Yusuf P.U., dan M. Hatta D. Pembuatan Briket Arang Dari Campuran Buah Bintaro dan Tempurung Kelapa Menggunakan Perekat Amilum. JurnalTeknik Kimia Fakultas Teknik Universitas Sriwijaya. 2012 : 18 (1) : 24-29
  7. Haniffudin Nurdiansah dan Diah Susanti Pengaruh Variasi Temperatur Karbonisasi dan Temperatur Aktivasi Fisika dari Elektroda Karbon Aktif Tempurung Kelapa dan Tempurung Kluwak Terhadap Nilai Kapasitansi Electric Double Layer Capacitor(EDLC)Jurnal Teknik POMITS , 2013: 2 (1) : F13-F18
  8. Hamdaoui, O dan Mahdi C. Removal of Methylene Blue from Aqueous Solutions by Wheat Bran. Acta Chim. 2006 : 54 (1) : 407-418
  9. Suarsa, I.W.,Suarya, P., dan Kurniawati, I. Optimasi Jenis Pelarut dalam Ekstraksi Zat Warna Alam Dari Batang Pisang Kepok (Musa paradiasiaca L. cv kepok ) dan Batang Pisang Susu ( Musa paradiasiaca L. cv susu). Journal of Chemistry. 2011 : 5(1): 72-80
  10. Firdaus, M.L., Krisnanto, N., Alwi, W., Muhammad, R., dan Serunting, M.A. Adsorption of Textile Dye by Activated Carbon Made from Rice Straw and Palm Oil Midrib. Aceh International Journal of Science and Technology. 2017 : 7(1): 1-7
  11. Sastrawidana, I.D.K., Bibiana, W.L., Anas M. F., dan Dwi A.S. Pengolahan Limbah Tekstil Sistem Kombinasi Anaerobik-Aerobik Menggunakan Biofilm Bakteri Konsorsium Dari Lumpur Limbah Tekstil. Jurnal Ilmu Lingkungan. 2012 : 3 (2) : 55-60
  12. Sari, R.A. M. Lutfi Firdaus., Rina Elvia. Penentuan Kesetimbangan, Termodinamika dan Kinetika Adsorpsi Arang Aktif Tempurung Kelapa Sawit Pada Zat Warna Reactive Red dan Direct Blue. Alotrop. 2017: 1 (1) : 10-14
  13. Syauqiah I., Mayang A., dan Hetty A.K. Analisis Variasi Waktu Kontak dan Kecepatan Pengaduk Pada Proses Adsorpsi Limbah Logam Berat dengan Arang Aktif. Info Teknik. 2011 : 12 (1) : 11-20.
  14. Puspita M., M. Lutfi Firdaus, Nurhamidah., Pemanfaatan Arang Aktif Sabut Kelapa Sawit Sebagai Adsorben Zat Warna Sintetis Reactive Red-120 dan Direct Green-26. Alotrop. 2017 : 1 (1) : 75.79.
  15. Madina, F.E, Rina Elvia, I Nyoman Chandra, . Analisis Kapasitas Adsorpsi Silika dari Pasir Pantai Panjang Bengkulu Terhadap Pewarna Rhodamine B. Alotrop , 2017, 1(2): 98-101
  16. Apriyanti, H., I Nyoman Candra, Elvinawati , Karakterisasi Isoterm Adsorpsi Dari Ion Logam Besi (Fe) Pada Tanah Di Kota Bengkulu, Alotrop, 2018: 2(1): 14-19.
  17. Dermirbas, A. Pyrolysis of Ground Beech Wood in Irregular Heating Rate Conditions. Journal of Analytical and Applied Pyrolysis.2005 : 73 (1): 39-43.
  18. Sakkayawong N., Thiravetyan P., dan Nakbanpote W. Adsorption Mechanism of Synthetic Dye Wastewater By Chitosan. Journal of Colloid and Interface Science. 2005 : 286 (1) : 36-42.
  19. Kamal N. Pemakaian Adsorben Karbon Aktif Dalam Pengolahan Limbah Industri Batik. Jurnal Teknolologi Fakultas Teknik Universitas Pakuan. 2014 : 2 (1) : 77-80.
  20. Tabak, A. Baltas N, Afsin, B, Emirik, M, Caglar, B, dan Eren, E. Adsorption of Reactive Red 120 from Aqueous Solutionsby Cetylpiradinium-Bentonit. JournalChemistry Technology Biotechnology. 2010 : 85 (1) : 1199-1207.
  21. Nurafriyanti, Nopi, S. P., dan Isna S. Pengaruh Variasi pH dan Berat Adsorben dalam Pengurangan Konsentrasi Cr Total ada Limbah Artifisial Menggunakan Adsorben Ampas Daun Teh. Teknik Lingkungan. 2017 : 3 (1) : 56-65.
  22. Lyubchik, S. 2000. Comparison of TheThermodynamic Parameters Estimation for The Adsorpstion Process of The Metals from Liquid Phase on Activated Carbon. Portugal:Intech. ISBN: 978-953-307-563-1
  23. Beroeh, K. 2004. Pengaruh Suhu Karbonisasi terhadap Daya Serap Karbon Aktif dengan Aktivator ZnCl2 dari Serbuk Gergaji Kayu Jati. Jurnal Teknik Kimia UMJ.
  24. Atkins, P.W. 1999. Kimia Fisika Jilid 1 EdisiKeempat. Jakarta : Erlangga. ISBN : 979-411-381-6.