Composite is a material that is formed from a combination of two or more forming materials through an inhomogeneous mixing consisting of two parts, namely the matrix as a composite binder or protector and the filler as a composite filler. Pandan sea leaf (Pandanus tectorius) is one alternative natural material that can be used as a filler in making composites because it has a high cellulose content and has strong fiber properties. The purpose of this research was to describe the process of making composites with natural fiber fillers and characteristics of composites produced. Making composites through 4 steps, namely making sea pandanus leaf powder, making cellulose fraction, making polyethylene terephthalate (PET) plastic waste matrix, and making composite. Based on the results of the composite characterization research includes water content from 2.46% to 3.51%, density from 0.49 g/cm3 to 0.52 g/cm3, porosity from 10.02% to 24.06%, and absorption water that is 24.88% to 46.51%. The type of MPA 1 (30% filler cellulose sea pandanus leaves: 70% polyethylene terephthalate pellet matrix) had a moisture content that complies with SNI 01-4449-2006 that is 2.46%, the corresponding density value SNI 03-2105-2006 is 0.52 g/cm3, the porosity value that is in line with SNI 03-2105-2006 is 10.02%, and the absorption according to JIS A5905-2003 standard is 24.88%.
Article Details
Authors who publish in this journal agree with the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.
- Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).
- This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
References
- Armidion, R. dan Rahayu, T., 2018. Peningkatan Nilai Kuat Tarik Belah Beton dengan Campuran Limbah Botol Plastik Polyetylene Terephthalate (PET). Jurnal Konstruksia, 10(1): 117-126.
- BSN, 2006. SNI 01-4449-2006 tentang Standard Nasional Papan Serat. Jakarta: Badan Standardisasi Nasional.
- BSN, 2006. SNI 03-2105-2006 tentang Standard Nasional Papan Partikel. Jakarta: Badan Standardisasi Nasional.
- Dewi, I. P. dan Sofia, L. A., 2020. Pengembangan Bisnis Pembibitan Mangrove untuk Abrasi Pantai Di Desa Pagatan Besar, Kalimantan Selatan. PRO SEJAHTERA (Prosiding Seminar Nasional Pengabdian kepada Masyarakat), 2(1): 74-81.
- Fathanah, U., 2011. Kualitas Papan Komposit dari Sekam Padi dan Plastik HDPE Daur Ulang Menggunakan Maleic Anhydride (MAH) sebagai Compatibilizer. Jurnal Rekayasa Kimia dan Lingkungan , 8(2): 53-59.
- Gulo, W. Y., Sinuhaji, P. dan Syukur, M., 2013. Pembuatan dan Karakterisasi Komposit Serat Palem Saray dengan Matriks Epoksi. Jurnal Saintia Fisika, 3(1) : 1-5. https://media.neliti.com/media/publications/221330-pembuatan-dan-karakterisasi-komposit-ser.pdf.
- Gusmailina, 2010. Peningkatan Teknik Pengolahan Pandan (Bagian 1) : Pewarnaan dan Pengeringan. Jurnal Penelitian Hasil Hutan, 28(1): 66-76.
- Hairiyah, N., Amalia, R. dan Widyastuti, A., 2017. Pembuatan Mikrokomposit Purun Tikus (Eleocharis Dulcis) dan Eceng Gondok (Eichornia Crassipes) Sebagai Filler dengan Limbah Plastik Polyethylene Terephthalate (PET) Sebagai Matrix. Jurnal Teknologi Agro-Industri, 4(2): 61-72.
- Hairiyah, N., Nuryati dan Meldayanoor, 2017. Karakteristik Mekanik Mikrokomposit Dari Tongkol Jagung Dan Limbah Plastik Polipropilene. Jurnal Teknologi Agro-Industri, 4(1): 1-10.
- Izaak, F. D., Rauf, A. F. dan Lumintang, R., 2013. Analisis Sifat Mekanik dan Daya Serap Air Material Komposit Serat Rotan. Jurnal Online Poros Teknik Mesin, 2(2). https://ejournal.unsrat.ac.id/index.php/poros/article/view/2988/2533, 1-12.
- Manurung, S. X., Sinuhaji, P. dan Syukur, M., 2013. Pembuatan dan Karakterisasi Komposit Serat Palem Saray dengan Matriks Poliester. Jurnal Saintia Fisika, 4(1).
- Matheus, J., Irawan, Y. S. dan Soenoko, R., 2013. Pengaruh Perlakuan Silane dan NaOH pada Permukaan Serat Kontinyu Limbah Epulur Sagu (Metroxylon Sp) Terhadap Daya Serap Air dan Kekuatan Bending. Jurnal Rekayasa Mesin, 4(2): 212-219.
- Nopriantina, N. dan Astuti, 2013. Pengaruh Ketebalan Serat Pelepah Pisang Kepok (Musa Paradisiaca) Terhadap Sifat Mekanik Material Komposit Poliester-Serat Alam. Jurnal Fisika Unand, 2(3): 195-203.
- Okatama, I., 2016. Analisa Peleburan Limbah Plastik Jenis Polyethylene Terphtalate (PET) Menjadi Biji Plastik Melalui Pengujian Alat Pelebur Plastik. Jurnal Teknik Mesin, 5(3): 20-24.
- Rita, R., Setyawati, D. dan Usman, F. H., 2015. Sifat Fisik dan Mekanik Papan Komposit dari Batang Singkong dan Limbah Plastik Berdasarkan Pelapisan dan Komposisi Bahan Baku. Jurnal Hutan Lestari, 2(3): 337-346.
- Saputra, A., Wicaksono, M. dan Irsan, 2017. Pemanfaatan Minyak Goreng Bekas untuk Pembuatan Biodiesel Menggunakan Katalis Zeolit Alat Teraktivasi. Jurnal Chemurgy, 1(2): 1-6.
- Sari, N. M., 2011. Sifat Fisik dan Mekanik Papan Partikel dari Limbah Plastik Jenis Hdpe (High Density Polyetylene) dan Ranting/Cabang Karet (Hevea Brasiliensis Muell.Arg). Jurnal Riset Industri Hasil Hutan, 3(1): 7-14.
- Sriwita, A., 2014. Pembuatan dan Karakterisasi Sifat Mekanik Bahan Komposit Serat Daun Nenas-Polyester Ditinjau dari Fraksi Massa dan Orientasi Serat. Jurnal Fisika Unand, 3(1): 30-36.
- Sulardjaka, Wibowo, D., Arijanto dan Setiaji , E., 2011. Pengaruh Temperatur Tuang pada Proses Pengecoran Stir Casting Terhadap Densitas dan Porositas Komposit Alumunium Diperkuat Serbuk Besi. Jurnal Teknik Mesin, 13(3): 19-21.
- Sunardi, Fawaid, M. dan Noor, F. R., 2015. Variasi Campuran Fly Ash Batubara untuk Material Komposit. Jurnal Teknik Mesin UNTIRTA, 1(1): 90-102.
- Taufik, C. dan Astuti, 2014. Sintesis dan Karakterisasi Sifat Mekanik Serta Struktur Mikro Komposit Resin yang Diperkuat Serat Daun Pandan Alas (Pandanus Dubius). Jurnal Fisika Unand, 3(1): 41-47.
- Widiartha, I., Sari, N. dan Sujita, 2012. Study Kekuatan Bending dan Struktur Mikro Komposit Polyethylene yang Diperkuat Oleh Hybrid Serat Sisal dan Karung Goni. Jurnal Dinamika Teknik Mesin, 2(2): 92-99.
- Zulkifli, Hermansyah, H. dan Mulyanto, S., 2018. Analisa Kekuatan Tarik dan Bentuk Patahan Komposit Serat Sabuk Kelapa Bermatriks Epoxy terhadap Variasi Fraksi Volume Serat. Jurnal Teknologi Terpadu, 6(2): 90-95.
References
Armidion, R. dan Rahayu, T., 2018. Peningkatan Nilai Kuat Tarik Belah Beton dengan Campuran Limbah Botol Plastik Polyetylene Terephthalate (PET). Jurnal Konstruksia, 10(1): 117-126.
BSN, 2006. SNI 01-4449-2006 tentang Standard Nasional Papan Serat. Jakarta: Badan Standardisasi Nasional.
BSN, 2006. SNI 03-2105-2006 tentang Standard Nasional Papan Partikel. Jakarta: Badan Standardisasi Nasional.
Dewi, I. P. dan Sofia, L. A., 2020. Pengembangan Bisnis Pembibitan Mangrove untuk Abrasi Pantai Di Desa Pagatan Besar, Kalimantan Selatan. PRO SEJAHTERA (Prosiding Seminar Nasional Pengabdian kepada Masyarakat), 2(1): 74-81.
Fathanah, U., 2011. Kualitas Papan Komposit dari Sekam Padi dan Plastik HDPE Daur Ulang Menggunakan Maleic Anhydride (MAH) sebagai Compatibilizer. Jurnal Rekayasa Kimia dan Lingkungan , 8(2): 53-59.
Gulo, W. Y., Sinuhaji, P. dan Syukur, M., 2013. Pembuatan dan Karakterisasi Komposit Serat Palem Saray dengan Matriks Epoksi. Jurnal Saintia Fisika, 3(1) : 1-5. https://media.neliti.com/media/publications/221330-pembuatan-dan-karakterisasi-komposit-ser.pdf.
Gusmailina, 2010. Peningkatan Teknik Pengolahan Pandan (Bagian 1) : Pewarnaan dan Pengeringan. Jurnal Penelitian Hasil Hutan, 28(1): 66-76.
Hairiyah, N., Amalia, R. dan Widyastuti, A., 2017. Pembuatan Mikrokomposit Purun Tikus (Eleocharis Dulcis) dan Eceng Gondok (Eichornia Crassipes) Sebagai Filler dengan Limbah Plastik Polyethylene Terephthalate (PET) Sebagai Matrix. Jurnal Teknologi Agro-Industri, 4(2): 61-72.
Hairiyah, N., Nuryati dan Meldayanoor, 2017. Karakteristik Mekanik Mikrokomposit Dari Tongkol Jagung Dan Limbah Plastik Polipropilene. Jurnal Teknologi Agro-Industri, 4(1): 1-10.
Izaak, F. D., Rauf, A. F. dan Lumintang, R., 2013. Analisis Sifat Mekanik dan Daya Serap Air Material Komposit Serat Rotan. Jurnal Online Poros Teknik Mesin, 2(2). https://ejournal.unsrat.ac.id/index.php/poros/article/view/2988/2533, 1-12.
Manurung, S. X., Sinuhaji, P. dan Syukur, M., 2013. Pembuatan dan Karakterisasi Komposit Serat Palem Saray dengan Matriks Poliester. Jurnal Saintia Fisika, 4(1).
Matheus, J., Irawan, Y. S. dan Soenoko, R., 2013. Pengaruh Perlakuan Silane dan NaOH pada Permukaan Serat Kontinyu Limbah Epulur Sagu (Metroxylon Sp) Terhadap Daya Serap Air dan Kekuatan Bending. Jurnal Rekayasa Mesin, 4(2): 212-219.
Nopriantina, N. dan Astuti, 2013. Pengaruh Ketebalan Serat Pelepah Pisang Kepok (Musa Paradisiaca) Terhadap Sifat Mekanik Material Komposit Poliester-Serat Alam. Jurnal Fisika Unand, 2(3): 195-203.
Okatama, I., 2016. Analisa Peleburan Limbah Plastik Jenis Polyethylene Terphtalate (PET) Menjadi Biji Plastik Melalui Pengujian Alat Pelebur Plastik. Jurnal Teknik Mesin, 5(3): 20-24.
Rita, R., Setyawati, D. dan Usman, F. H., 2015. Sifat Fisik dan Mekanik Papan Komposit dari Batang Singkong dan Limbah Plastik Berdasarkan Pelapisan dan Komposisi Bahan Baku. Jurnal Hutan Lestari, 2(3): 337-346.
Saputra, A., Wicaksono, M. dan Irsan, 2017. Pemanfaatan Minyak Goreng Bekas untuk Pembuatan Biodiesel Menggunakan Katalis Zeolit Alat Teraktivasi. Jurnal Chemurgy, 1(2): 1-6.
Sari, N. M., 2011. Sifat Fisik dan Mekanik Papan Partikel dari Limbah Plastik Jenis Hdpe (High Density Polyetylene) dan Ranting/Cabang Karet (Hevea Brasiliensis Muell.Arg). Jurnal Riset Industri Hasil Hutan, 3(1): 7-14.
Sriwita, A., 2014. Pembuatan dan Karakterisasi Sifat Mekanik Bahan Komposit Serat Daun Nenas-Polyester Ditinjau dari Fraksi Massa dan Orientasi Serat. Jurnal Fisika Unand, 3(1): 30-36.
Sulardjaka, Wibowo, D., Arijanto dan Setiaji , E., 2011. Pengaruh Temperatur Tuang pada Proses Pengecoran Stir Casting Terhadap Densitas dan Porositas Komposit Alumunium Diperkuat Serbuk Besi. Jurnal Teknik Mesin, 13(3): 19-21.
Sunardi, Fawaid, M. dan Noor, F. R., 2015. Variasi Campuran Fly Ash Batubara untuk Material Komposit. Jurnal Teknik Mesin UNTIRTA, 1(1): 90-102.
Taufik, C. dan Astuti, 2014. Sintesis dan Karakterisasi Sifat Mekanik Serta Struktur Mikro Komposit Resin yang Diperkuat Serat Daun Pandan Alas (Pandanus Dubius). Jurnal Fisika Unand, 3(1): 41-47.
Widiartha, I., Sari, N. dan Sujita, 2012. Study Kekuatan Bending dan Struktur Mikro Komposit Polyethylene yang Diperkuat Oleh Hybrid Serat Sisal dan Karung Goni. Jurnal Dinamika Teknik Mesin, 2(2): 92-99.
Zulkifli, Hermansyah, H. dan Mulyanto, S., 2018. Analisa Kekuatan Tarik dan Bentuk Patahan Komposit Serat Sabuk Kelapa Bermatriks Epoxy terhadap Variasi Fraksi Volume Serat. Jurnal Teknologi Terpadu, 6(2): 90-95.